国法奥迪耐磨焊条《VAUTID》
发布时间 2018-09-11 16:45:56
产品描述
| FCAW堆焊药芯焊丝 | ||||||
|
产品
|
混合气
|
CO2
|
SOS
|
成份
|
强度KSI
|
硬度 HRC
|
|
100HC
|
|
|
2.4
2.8 |
34.0% Mn Si Cr Mo
|
|
低碳钢二层58-62 锰钢二层51-55 |
|
100HD
|
|
2.8
3.2 |
36.5% Mn Si Cr
|
|
55-62
|
|
|
101HC
|
1.2
|
1.6
|
1.6
2.0 |
26.0%C Mn Si Cr
|
|
低碳钢一层55-64
低碳钢二层59-64 |
|
102
|
l.2
|
1.6
|
1.6
|
14.0%C Mn Si Cr Mo V
|
|
48-53
|
|
105-G
|
1.6
|
|
|
7.00%C Mn Si Cr Mo
|
|
41-46
|
|
110
|
l.2
|
1.6
|
1.6/2.4 2.8 |
35.0%C Mn Si Cr Ni
|
T.S.119 Y.S.76.4
EL40% |
钢板多层17BHN
加硬达到55BHN |
|
117
|
|
|
1.6/2.4
|
17.0%C Mn Si Cr Mo Cu
|
|
低碳钢三层43-45
锰钢二层38-40 |
|
121
|
l.2
|
1.6
|
1.6/2.4
2.8 |
21.0%C Mn Si Cr
|
|
锰钢一层40-44
锰钢二层47-51 |
|
131
|
|
|
1.6
2.8 |
33.0%C Mn Si Cr Mo
|
|
低碳钢二层40-45
锰钢二层37-40 |
|
134
|
|
2.8
|
2.8
|
33.0%C Mn Si Cr Mo
|
|
低碳钢二层56-60
锰钢二层45-50 |
|
135
|
|
|
1.6
|
35.0%C Mn Si Cr Mo
|
|
1020碳钢二层54- 62
|
|
965-G |
l.2
|
1.6
|
1.6
|
10.0%C Mn Si Cr
|
|
56-60
|
|
965AP-G
|
l.2
1.6 |
|
|
11.0%C Mn Si Cr Mo
|
|
二层57-62
|
|
BUILD UP
|
l.2
|
1.6
|
1.6/2.4
2.8 |
4.00%C Mn Si Cr Mo
|
|
0.10%C二层24-28 0.80%C二层38-42 |
|
BUILD
UP AP-G |
l.2 1.6 |
|
|
4.00%C Mn Si Cr Mo
|
|
二层24-27
|
|
DYNAMANG |
|
1.2
1.6 |
1.2/1.6
2.8 |
20.0%C Mn Cr Ni
|
T.S.120 Y.S.70
EL42% |
钢板多层200BHN
加硬达到500BHN |
|
NICROMANG |
|
1.6
|
1.6/2.4
2.8 |
23.0%C Mn Cr Ni
|
T.S.120 Y.S.70
EL42% |
钢板多层200BHN
加硬达到500BHN |
|
SUPER BUILD UP
|
l.2
|
1.6
|
1.6
2.8 |
5.00%C Mn Si Cr Mo
|
|
二层35-40
|
|
TRACKWEAR
|
|
1.6
|
1.6/2.0
2.8 |
19.0%C Mn V
|
T.S.128 Y.S.85
EL42% |
钢板多层200BHN
加硬达到500BHN |